New Strategy Improves Stability of Platinum Group Metal Catalysts
  English.dicp.cas.cn    Posted:2021-05-18    From:DNL2005

Recently, a group led by Prof. WANG Junhu from the Dalian Institute of Chemical Physics (DICP) of the Chinese Academy of Sciences (CAS), in collaboration with Prof. AO Zhimin from the Guangdong University of Technology and Prof. ZHANG Binsen from the Institute of Metals of CAS, constructed a novel type of strong metal-support interaction (SMSI) through the melamine/urea catalyst modification and oxidation atmosphere calcination, and developed a new strategy to improve the stability of platinum group metals (PGMs) catalysts.

This study was published in ACS Catalysis on May 4.

The induced overlayer of SMSI often covers several catalytic active sites, leading to catalysts inactive in a degree. Moreover, the retreat of the overlayer upon reverse atmosphere treatment curtails the effect of SMSI on enhancing the catalytic performance of underlying metals, especially at elevated temperatures.

The classical SMSI induced by reduction atmosphere calcination between transition metal oxides and PGMs has been investigated. However, the encapsulation on the same catalysts occurred under oxidation condition is still unclear.

Schematically shown the differences of classical and novel SMSIs separately induced by reduction atmosphere calcination and melamine/urea modification and oxidation atmosphere calcination in the titania-supported platinum catalyst (Image by LIU Shaofeng)

The researchers found the evidence that PGMs nanoparticles could be encapsulated by an amorphous and permeable TiOx cover layer on titania-supported catalysts under oxidative atmosphere driven by melamine/urea. It was contrary to the condition needed for classical SMSI between Pt and TiO2.

Moreover, the formed overlayer was stabilized against re-oxidation at 400-600 °C in air, in sharp contrast to the retreat of TiOx overlayer by subsequent oxidation treatment in classical SMSI. And the formation mechanism of this kind of encapsulation was different from that of classical SMSI.

"The new strategy was further demonstrated on titania-supported Pd and Rh nanoparticles, and it provides a promising new way for designing supported PGMs-based catalysts with high activity and stability," said Prof. WANG. (Text by LIU Shaofeng)

DALIAN INSTITUTE OF CHEMICAL PHYSICS, CHINESE ACADEMY OF SCIENCES

Welcome
Opportunities
Education

Campus Map
Contact

中文

Dalian Institute of
Chemical Physics, CAS
457 Zhongshan Road
Dalian, China 116023

Copyright 1999-2020. Dalian Institute of Chemical Physics, Chinese Academy of Sciences. All rights reserved.